EN-GJS-450-10, ASTM A536 65-45-12, Ductile Iron, SG Iron Chemical Composition, Mechanical and Physical Properties

EN-GJS-450-10, ASTM A536 65-45-12, Ductile Iron, SG Iron Chemical Composition, Mechanical and Physical Properties

EN-GJS-450-10 (ASTM A536 65-45-12) is an excellent ductile iron (SG iron) material grade. It has comparatively high tensile strength, high elongation, and good impact resistance. So, this cast iron grade has very wide application.

ZHY Foundry has producing this material grades for many years, and herein, we share its chemical composition, mechanical and physical properties.

1. Equivalent Material Grades of Ductile Iron GJS-450

The equivalent grades of EN 1563 EN-GJS-450-10 are ASTM A536 65-45-12, FCD400, FGS400, FGE42-12, FNG42-12, GS400-12, 60-42-10, QT450-10, ISO 450-10. Although some grades just require elongation 10%, the iron foundries just need to adjust the chemical composition to make the elongation a little higher, then they will meet the requirement.

2. Chemical Composition of SG Iron, Ductile Iron GJS-450

According to all international material standards, the chemical composition should not be taken as the inspection standard, unless the clients have special requirements. However, by our experience, the approximate chemical components of ductile iron GJS-450 should be as C: 3.50-4.00, Si: 2.20-2.90, Mn: 0.3-0.6, P: 0.03-0.06, S: 0.02-0.040, Mg: 0.020-0.060.

3. Mechanical & Physical Properties of Ductile Iron GJS-450

Tensile Strength ≥ 450 MPa. Yield Strength ≥ 310 MPa. Elongation ≥ 10%.

As for A536 65-45-12, its elongation ≥ 12%. Other requirements will be as same as GJS-450.

There is no strict stipulation to the hardness of GJS-450, however, normal hardness range should be 160 – 210 BH (Brinell Hardness).

4. Main Application of Ductile Iron GJS-450

Because of the comparatively high elongation, this GJS-450 ductile iron could be used for producing impact resistance casting parts. In addition, it has good low temperature impact resistance, and good hardness, so it has been used for producing plow point, blade plough, furrow plough, furrow plough, plough pile, differential shell, valve body, and high pressure cylinder.

The followings are some ductile iron castings we produced.

iron castings of valves EN GJS 450 10, ASTM A536 65 45 12, Ductile Iron, SG Iron Chemical Composition, Mechanical and Physical Propertiesiron castings of building machines EN GJS 450 10, ASTM A536 65 45 12, Ductile Iron, SG Iron Chemical Composition, Mechanical and Physical Propertiescast iron compressor bodies EN GJS 450 10, ASTM A536 65 45 12, Ductile Iron, SG Iron Chemical Composition, Mechanical and Physical Propertiesplow points EN GJS 450 10, ASTM A536 65 45 12, Ductile Iron, SG Iron Chemical Composition, Mechanical and Physical Properties

 

Do you want to have a look at our products?

Yes, why not                         No,thank you

google plus EN GJS 450 10, ASTM A536 65 45 12, Ductile Iron, SG Iron Chemical Composition, Mechanical and Physical Propertieslinkedin EN GJS 450 10, ASTM A536 65 45 12, Ductile Iron, SG Iron Chemical Composition, Mechanical and Physical Propertiespinterest EN GJS 450 10, ASTM A536 65 45 12, Ductile Iron, SG Iron Chemical Composition, Mechanical and Physical Propertiesfacebook EN GJS 450 10, ASTM A536 65 45 12, Ductile Iron, SG Iron Chemical Composition, Mechanical and Physical Propertiestwitter EN GJS 450 10, ASTM A536 65 45 12, Ductile Iron, SG Iron Chemical Composition, Mechanical and Physical Propertiesyahoo EN GJS 450 10, ASTM A536 65 45 12, Ductile Iron, SG Iron Chemical Composition, Mechanical and Physical Propertiesgoogle EN GJS 450 10, ASTM A536 65 45 12, Ductile Iron, SG Iron Chemical Composition, Mechanical and Physical Propertiesbox EN GJS 450 10, ASTM A536 65 45 12, Ductile Iron, SG Iron Chemical Composition, Mechanical and Physical Propertiesamazon EN GJS 450 10, ASTM A536 65 45 12, Ductile Iron, SG Iron Chemical Composition, Mechanical and Physical Propertiesfavicon EN GJS 450 10, ASTM A536 65 45 12, Ductile Iron, SG Iron Chemical Composition, Mechanical and Physical Properties
  • Posted on October 28, 2013 - 8:46 am
  • By Alex Guan
  • Posted in


Copyright © 2012 zhyfoundry.com